產品(pin)名(ming)稱(cheng): 17-4PH-YB
產品描述:
采用水(shui)霧(wu)化(hua)(hua)17-4PH不銹鋼粉末制備(bei)的(de)金(jin)屬粉末注(zhu)射(she)(she)成型專用喂料(liao),僅適(shi)用于(yu)注(zhu)射(she)(she)成型和催化(hua)(hua)脫脂工藝制造各類復雜形狀17-4PH不銹鋼結(jie)構(gou)件。
燒結后典(dian)型成分(%) :
C | Cr | Ni | Cu | Nb | Mn | Si | Fe |
≤0.07 |
15.0-17.5 | 3-5 |
3-5 |
0.15-0.45 |
≤1 |
≤1 |
Bal |
注(zhu)射原料(liao)性(xing)能參數(shu):
項目 | 單位 | 典(dian)型值 | 參(can)考范圍 | 測試方法 |
熔融指數(shu) | g/10min | 900 | 500-2000 | ISO 1133(190℃.21.6Kg) |
燒結密度(du) | g/cm3 | 7.67 | 7.55-7.75 | ISO 3369 |
標準(zhun)收縮率 | / | 1.165 | 1.162-1.168 | 模具尺寸/產品尺寸 |
燒結部件的物理(li)機械性能:
項目 | 燒結態(tai) |
密度 | ≥7.60/cm3 |
屈服強度 | ≥730Mpa |
極(ji)限拉(la)伸強度 | ≥960mpa |
延(yan)伸率 | ≥6% |
硬度 | 260-350 HV10 |
Product name: 1 7 -4PH-YB
Product description:Special injection for metal powder injection molding prepared by water atomization of 17-4PH stainless steel powder is only suitable for injection molding and catalytic degreasing process to manufacture various complex shapes of 17-4PH stainless steel structural parts.
Typical composition after sintering (%) :
C | Cr | Ni | Cu | Nb | Mn | Si | Fe |
≤0.07 |
15.0-17.5 | 3-5 |
3-5 |
0.15-0.45 |
≤1 |
≤1 |
Bal |
Injection raw material performance parameters:
Project | Unit | Typical valve | Reference range | Testing method |
Melt Index | g/10min | 900 | 500-2000 | ISO 1133(190℃.21.6Kg) |
Sintering density | g/cm3 | 7.67 | 7.55-7.75 | ISO 3369 |
Standard shrinkage | / | 1.165 | 1.162-1.168 | Mold size / product size |
Physical and mechanical properties of sintered parts:
Project | Sintered statec |
Density | ≥7.60/cm3 |
Yield Strength | ≥730Mpa |
Ultimate tensile strength | ≥960mpa |
Elongation | ≥6% |
hardness | 260-350 HV10 |