產品名稱: PANACEA-YB
產品描述:
采用(yong)霧化PANACEA高氮(dan)無(wu)鎳不銹鋼粉末(mo)制備的金屬粉末(mo)注射成(cheng)型專用(yong)喂(wei)料(liao),僅(jin)適用于(yu)注(zhu)射成型(xing)和催化脫脂工藝制造各類復雜形狀高氮無鎳不銹(xiu)鋼結構(gou)件(jian)。
燒結后(hou)典(dian)型(xing)成分(%)
C | N | Cr | Mo | Mn | Si | Fe |
≤0.2 | 0.75-0.90 | 16.5-17.5 | 3.0-3.5 | 10-12 | ≤1 | Bal |
注射原料性能參數
項(xiang)目 | 單位 | 典型值 | 參考范圍 | 測試方法 |
熔融(rong)指數 | g/10min | 600 | 300-900 | ISO 1133(190℃.21.6Kg) |
燒結密(mi)度(du) | g/cm3 | 7.6 | 7.5-7.7 | ISO 3369 |
標準收縮(suo)率 | / | 1.165 | 1.162-1.168 | 模具尺寸/產品尺寸 |
燒結部件的物(wu)理(li)機械性能
項(xiang)目 | 燒結態 |
密度 | ≥7.5/cm3 |
屈服強度 | ≥700Mpa |
極(ji)限拉伸(shen)強(qiang)度(du) | ≥1000mpa |
延伸率 | ≥35% |
硬度 | 270-330 HV10 |
Product name: PANACEA-YB
Product description:
The special injection of metal powder injection molding prepared by atomizing PANACEA high-nitrogen nickel-free stainless steel powder is only suitable for injection molding and catalytic degreasing process to manufacture various complex shape high-nitrogen nickel-free stainless steel structural parts.
Typical composition after sintering (%) :
C | N | Cr | Mo | Mn | Si | Fe |
≤0.2 | 0.75-0.90 | 16.5-17.5 | 3.0-3.5 | 10-12 | ≤1 | Bal |
Injection raw material performance parameters:
Project |
Unit |
Typical valve |
Reference range |
Testing method |
Melt Index |
g/10min | 600 | 300-900 | ISO 1133(190℃.21.6Kg) |
Sintering density |
g/cm3 | 7.6 | 7.5-7.7 | ISO 3369 |
Standard shrinkage |
/ | 1.165 | 1.162-1.168 | Mold size / product size |
Physical and mechanical properties of sintered parts:
Project |
Sintered state |
Density |
≥7.5/cm3 |
Yield Strength |
≥700Mpa |
Ultimate tensile strength |
≥1000mpa |
Elongation |
≥35% |
hardness |
270-330 HV10 |